How to Judge the Performance Criteria of Alslag Remover Fluxes

Next, we will introduce in detail how to judge the performance of slag remover in steelmaking.
The performances of aluminium slag remover fluxes are reflected in slag removal effect, usage, dosage and iron loss.

1.Aluminum slag remover fluxes put into aluminium water ladle should have certain stickiness, be able to agglomerate slag into piles and have a certain strength. It is convenient to pick the slag out or pick it out at one time, saving the time of picking up slag (about 12 seconds, reducing power loss (electric furnace and temperature reduction).

2.2. The method of use is simple and does not need to be sown evenly.

3. Dosage: At present, the minimum dosage is 2 to 3 kilograms of aluminium slag remover fluxes per ton of aluminium water.

4. Enwrapping aluminium loss: The more aluminium water is lost along with the scraping of slag, the better aluminium slag remover fluxes can keep aluminium loss at about 1 kg per ton of aluminium treated.

5.Rapid reaction, certain expansibility, rapid projection, no need to stir.

6. It does not contain substances that change the composition of aluminium and water, so as to avoid affecting the properties of cast aluminium.

7.Aluminum slag remover fluxes do not raise dust, improve the working environment, do not contain toxic substances, and reduce the risk of occupational diseases among workers.

8. After cooling, the slag is brittle and easy to recover the wrapped aluminium.

JINZHOU SATA FUSED FLUXES AND NEW MATERIALS FACTORY
is a professional enterprise specializing in the production and development of various metal fluxes, aluminum alloy additives, aluminum slag remover fluxes, various aluminum-based master alloys, cast aluminum alloys, and supporting equipment for molten aluminum. The company combines the characteristics of the industry to develop a variety of new products, can customize special specifications of products according to customer requirements, and provide casting technology solutions.

Jinzhou Sata Fused Fluxes and New Materials Factory (SATA for short), is a professional aluminium covering flux industry with integrated capability of product research & development, manufacture, business management and services. If you want to know more details, just feel free to contact us!

评论

发表评论

此博客中的热门博文

Main Components of Deslagging Agent

图片
The main components of deslagging agent are potassium, chlorine and fluorine. Among them, JKCZ-1 and JKCZ-2 all contain sodium, while JKCZ-3 does not contain sodium. The deslagging agent  produced by our company alleviates the disadvantageous factors of iron oxide to melt lime. The slag remover is adopting pre-melting process of calcium oxide, alumina and iron oxide and by pressing ball process. Because of the pre-melting process, calcium oxide is melted in advance, and calcium ferrite and calcium aluminate are formed in advance with iron oxide and alumina, which can reduce the heat needed for converter melting and shorten the melting time. The composite minerals formed by ferric oxide and alumina and calcium oxide have low melting point and fast melting speed, which can promote the quick melting of lime in converter. The alumina content of this product is different from that of pre-melting refining agent, and its price is relatively low. The product can reduce the use of conv...
阅读全文

Degassing Flux

图片
Degassing Flux  (SATA-PF-350) General Description of Degassing Flux (SATA-PF-350) Practice has proved that the hydrogen is the main cause of the pores in the aluminium alloy, the pores not only reduce the actual cross-sectional area of the casting, but also the source of the crack, so it is important part that removing the hydrogen during the smelting process. SATA-degassing flux   also name aluminum degassing flux   is   a kind of traditional high efficiency degassing flux for aluminium and its alloys, it used for removing hydrogen and oxides from the aluminium melting. Application of Degassing Flux (SATA-PF-350) Plunge suitable quantity flux to the bottom (100mm from the bottom is better) of the melt, evenly and slowly remove the lunch, make the flux fully react with aluminium molten, stand or stir the molten for 10-15 min, the hydrogen and oxide will be taken out of aluminium molten. Advantage of Degassing Flux (SATA-PF-350) Easy operation, There ...
阅读全文

Covering Flux Characteristics You Don't Know

图片
  The covering flux is a covering material that can extend the solidification time of the molten metal in the riser and cover the surface of the molten metal in the riser during casting production. There are two types of covering fluxes: thermal insulation covering fluxes and heat-generating covering fluxes.  We provide refining flux , alumina ceramic foam filter , grain refiner for aluminium , magnesium flux , electrode flux material an d s o on.   The characteristics of the covering flux are as follows:   1. The thermal insulation covering flux is made of low thermal conductivity materials, such as expanded perlite, expanded graphite, etc.   2. In addition to the low thermal conductivity material, the heating covering flux is added with a certain proportion of heating materials. Under the heat of the molten metal, the oxidant provides oxygen to oxidize the reducing agent and generates heat, thereby prolonging the solidification time of the molten metal in...
阅读全文