Selection of Chemical Composition of 6063 Aluminum Alloy

 6063 aluminum alloy is widely used in the construction of aluminum doors and windows and curtain wall frames. In order to ensure that the doors and windows have high wind pressure resistance, assembly performance, corrosion resistance and decorative performance, the comprehensive requirements for aluminum alloy profiles are far higher than those of industry. Profile standards, within the composition range of 6063 aluminum alloy specified in Chinese national standard GB / T3190, different values of chemical composition will result in different profile characteristics. When the range of chemical composition is large, the performance difference will be very large. The range fluctuates, so that the overall performance of the profile cannot be controlled. Therefore, it is preferable that the chemical composition of 6063 aluminum alloy becomes the most important part of producing high-quality aluminum alloy building profiles.

 

1. The role of alloying elements and its effect on properties 6063 aluminum alloy is a heat-strengthable strengthened alloy with medium strength in the AL-Mg-Si series Aluminium alloy. Mg and Si form the strengthening phase Mg2Si. The higher the content of Mg, the greater the amount of Mg2Si The more the heat treatment strengthens the effect, the higher the tensile strength of the profile, but the deformation resistance also increases, the plasticity of the alloy decreases, and the workability deteriorates.

 

The role and influence of Si: The amount of Si should be such that all Mg in the alloy can exist in the form of Mg2Si to ensure that the role of Mg is fully exerted. As the Si content increases, the alloy grains become finer, the metal fluidity increases, the casting properties become better, the heat treatment strengthening effect increases, the tensile strength of the profile increases, the plasticity decreases, and the corrosion resistance deteriorates.

 

2. Selection of Mg and Si content

1. Determination of the amount of Mg2Si: The role of Mg2Si in the alloy is that Mg2Si can be dissolved or precipitated with the change of temperature in the alloy, and exists in the alloy in different forms:

(1) the dispersed mass point dispersed in "B" Is a kind of unstable and will grow up with the increase of temperature.

(2) Excessive "B" is an intermediate metastable substance formed by "B", which will also increase with the temperature. When it grows up, (3) the precipitated substance "B" is a stable substance that grows from the substance B ', which mostly gathers at the grain boundaries and dendrite boundaries, and can play a strengthening role. The amount of Mg2Si is selected. Increases with the increase in the amount of Mg2Si

 

Jinzhou SATA Fused Fluxes and New Materials is a professionally leading manufacturer of foundry fluxes and chemicals. we can provide high-quality products such as Granular Flux, flux coating material, etc. In addition to that, we can also provide raw materials and auxiliary products for fluxes such as anhydrous magnesium chloride, magnesium chloride hexahydrate, fluorspar, synthetic cryolite, aluminum fluoride, potassium aluminum fluoride, Ali B grain refiner, ALTIC grain refiner, Al-Sr modifier, and other master alloy and metal additive, ceramic foam filters for casting.

 


评论

发表评论

此博客中的热门博文

Main Components of Deslagging Agent

图片
The main components of deslagging agent are potassium, chlorine and fluorine. Among them, JKCZ-1 and JKCZ-2 all contain sodium, while JKCZ-3 does not contain sodium. The deslagging agent  produced by our company alleviates the disadvantageous factors of iron oxide to melt lime. The slag remover is adopting pre-melting process of calcium oxide, alumina and iron oxide and by pressing ball process. Because of the pre-melting process, calcium oxide is melted in advance, and calcium ferrite and calcium aluminate are formed in advance with iron oxide and alumina, which can reduce the heat needed for converter melting and shorten the melting time. The composite minerals formed by ferric oxide and alumina and calcium oxide have low melting point and fast melting speed, which can promote the quick melting of lime in converter. The alumina content of this product is different from that of pre-melting refining agent, and its price is relatively low. The product can reduce the use of converte
阅读全文

Degassing Flux

图片
Degassing Flux  (SATA-PF-350) General Description of Degassing Flux (SATA-PF-350) Practice has proved that the hydrogen is the main cause of the pores in the aluminium alloy, the pores not only reduce the actual cross-sectional area of the casting, but also the source of the crack, so it is important part that removing the hydrogen during the smelting process. SATA-degassing flux   also name aluminum degassing flux   is   a kind of traditional high efficiency degassing flux for aluminium and its alloys, it used for removing hydrogen and oxides from the aluminium melting. Application of Degassing Flux (SATA-PF-350) Plunge suitable quantity flux to the bottom (100mm from the bottom is better) of the melt, evenly and slowly remove the lunch, make the flux fully react with aluminium molten, stand or stir the molten for 10-15 min, the hydrogen and oxide will be taken out of aluminium molten. Advantage of Degassing Flux (SATA-PF-350) Easy operation, There are two options. On
阅读全文

Drossing-Off Flux

图片
General Description And Function of Drossing-Off Flux Drossing-off flux is used to absorb oxides and non-metallic material, cleansing the metal and forming a good metal-free dross which can easily be removed.  Drossing-off fluxes agglomerate the oxides allowing easy removal from the surface of the melt. They are used to remove the dross with the minimum metal loss  Advantages of Drossing-Off Flux 1. Being exothermic fluxes, it can ensure that liquid aluminum trapped in the dross layer is returned to the melt. Produce dry powdery dross.  2. Provide further decrease of the flux melting point and improve its cleaning ability. Due to the high wetting capacity of fluoride compounds: it has a good effect of contributes to oxide – metal separation.  3. It helps recover metal from this slag layer , improving the yield of the process.
阅读全文