Why Magnesium Remover Flux is in Demand?





1. Considering the production cost, certain amount of aluminum scrap was added when manufacturing the aluminium alloy. The scrap is mainly the components of old automobiles and equipment.

The content of Magnesium will be too much higher in these scrap and the unsteady content of Magnesium occurs in some Magnesium alloy castings. This will failed in producing the required standard alloy ingots. In order to lower the magnesium content, some foundries wash by using high purity aluminium ingot. This method can achieve the goal .The large quantity of high purity aluminium ingot consumption increases the production cost and complicated the production process.

2. The effective operation of Magnesium removing is required if the Magnesium content is beyond stipulation in case of using aluminum scrap for alloying.

SATA magnesium remover flux gives you the best solution. Our flux is easy in use with its excellent performance. Removing magnesium and refining at same time.



Jinzhou Sata Fused Fluxes and New Materials Factory (SATA for short) is one of the most professional potassium aluminium fluoride suppliers. We provide Fluxes for Aluminum Alloy, Aluminum Alloying Tablet, Sodium Fluosilicate, flux coating material, grain refiners in aluminum alloy castings, Na3AIF6 and so on. Want to know more? Please contact us.




评论

发表评论

此博客中的热门博文

Main Components of Deslagging Agent

图片
The main components of deslagging agent are potassium, chlorine and fluorine. Among them, JKCZ-1 and JKCZ-2 all contain sodium, while JKCZ-3 does not contain sodium. The deslagging agent  produced by our company alleviates the disadvantageous factors of iron oxide to melt lime. The slag remover is adopting pre-melting process of calcium oxide, alumina and iron oxide and by pressing ball process. Because of the pre-melting process, calcium oxide is melted in advance, and calcium ferrite and calcium aluminate are formed in advance with iron oxide and alumina, which can reduce the heat needed for converter melting and shorten the melting time. The composite minerals formed by ferric oxide and alumina and calcium oxide have low melting point and fast melting speed, which can promote the quick melting of lime in converter. The alumina content of this product is different from that of pre-melting refining agent, and its price is relatively low. The product can reduce the use of conv...
阅读全文

Degassing Flux

图片
Degassing Flux  (SATA-PF-350) General Description of Degassing Flux (SATA-PF-350) Practice has proved that the hydrogen is the main cause of the pores in the aluminium alloy, the pores not only reduce the actual cross-sectional area of the casting, but also the source of the crack, so it is important part that removing the hydrogen during the smelting process. SATA-degassing flux   also name aluminum degassing flux   is   a kind of traditional high efficiency degassing flux for aluminium and its alloys, it used for removing hydrogen and oxides from the aluminium melting. Application of Degassing Flux (SATA-PF-350) Plunge suitable quantity flux to the bottom (100mm from the bottom is better) of the melt, evenly and slowly remove the lunch, make the flux fully react with aluminium molten, stand or stir the molten for 10-15 min, the hydrogen and oxide will be taken out of aluminium molten. Advantage of Degassing Flux (SATA-PF-350) Easy operation, There ...
阅读全文

Covering Flux Characteristics You Don't Know

图片
  The covering flux is a covering material that can extend the solidification time of the molten metal in the riser and cover the surface of the molten metal in the riser during casting production. There are two types of covering fluxes: thermal insulation covering fluxes and heat-generating covering fluxes.  We provide refining flux , alumina ceramic foam filter , grain refiner for aluminium , magnesium flux , electrode flux material an d s o on.   The characteristics of the covering flux are as follows:   1. The thermal insulation covering flux is made of low thermal conductivity materials, such as expanded perlite, expanded graphite, etc.   2. In addition to the low thermal conductivity material, the heating covering flux is added with a certain proportion of heating materials. Under the heat of the molten metal, the oxidant provides oxygen to oxidize the reducing agent and generates heat, thereby prolonging the solidification time of the molten metal in...
阅读全文